Orton Standard Cones Other products by Orton

Item No. OCSTD9
$12.70
Cone Number:   
Quantity:
More
Less
 

For more information about the use and behavior of Orton Pyrometric Cones, please download the PDF booklet from Orton:
Cones and Firing

 

Pyrometric cones measure heat-work (the effect of time and temperature). They are slender pyramids made from about 100 carefully controlled compositions. Each cone number is unique in measuring temperature within a small temperature range (less than 30°C). Cones measure the amount of heat absorbed over time. As the cone nears its maturing range, it softens and the tip begins to bend, drawn down by the influence of gravity.

Standard, or Large cones are used as witness cones to monitor the firing and verify temperature uniformity. A cone pack is necessary to support the cones during firing. If you have a kiln sitter on your kiln, you should use Junior cones.

Making the Cone Pack, by Vince Pitelka

Use care in making proper cone packs. Carelessly-made cone packs can cause inconvenience at best and a firing disaster at worst.

Form your cone pack on a piece of paper towel or newspaper so that the clay won’t stick. Roll out a coil of clay ½” to 5/8” diameter (no larger) and flatten it to about 3/8” thick (no thinner!). If there is a body reduction cone and/or any other low-temperature cones in a cone pack intended for midrange or highfire, always form an appropriate basin at the front end of the cone pack to catch the melting low-temperature cone. If there is more than one low-temperature cone in a midrange or highfire cone pack, form a trough around that portion of the cone-pack, or place the whole cone pack in a shallow pinched tray to catch the melting cones.

Place the lowest melting cone directly adjacent to and leaning towards one end of the cone pack or the molded catch-basin so that it falls unobstructed. Place each subsequent cone so that it falls towards the previous one. Place the cones directly next to each other with no space between them. Each cone should be pressed in as far as it will go, so that it displaces almost all clay beneath it. To determine the correct angle of tilt, hold a cone against the table surface and observe the angle. When you push the cone into the clay, make sure it tilts at the correct angle or slightly more. Make sure the cone number is visible from the side when the cone is in place.

After you press all the cones into the flattened coil of clay, squeeze the coil from both sides where it is thicker between each adjacent pair of cones in order to lock the cones in place. Trim off any excess clay at the ends of the cone pack.

If the cone pack is for a glaze-firing, thoroughly poke holes throughout the clay with a needle tool, especially in all the thicker areas. A cone pack that is for a bisque-firing with a slow preheat can go straight into the kiln without ventilation holes.

For additional information, please see Vince Pitelka's full notes on cone packs.

 

Pyrometric Cones (Orton Standard)
Temperature Equivalent Chart
(when heated at 150oC/hr*)


Warning! Do not view cones above earthenware temperature with the naked eye as this may cause cataracts. View through welders goggles - sunglasses are not suitable as they filter out UV, but not the infra-red, which is the damaging wavelength in this case!

Cone No. Centigrade Fahrenheit Visual Color
022 600 1112 Dull Red
021 614 1137
020 635 1175
019 683 1261
018 717 1322
017 747 1376
016 792 1457
015 804 1479
014 838 1540
013 852 1565
012 884 1623 Cherry Red
011 894 1641
010 900 1652
09 923 1693
08 955 1751 Orange
07 984 1803
06 999 1830
05 1046 1914
04 1060 1940
031/2 1080 1976
03 1101 2014
02 1120 2048
01 1137 2079
1 1154 2109 Yellow
2 1162 2124
3 1168 2134
4 1186 2167
5 1196 2185
6 1222 2232
7 1240 2264
8 1263 2305
9 1280 2336
10 1305 2381 White
11 1315 2399
12 1326 2419
13 1346 2455

 

Effect of Heating Rate, Hold Time, and Kiln Atmosphere

During the firing process, time, temperature and kiln atmosphere can influence the maturing of pyrometric cones, the same as any ceramic body.

 

Heating Rate

Heating rate will greatly affect the temperature at which a cone starts to deform, the rate of bending, and the end point (cone equivalent temperature) of the cone. Typically, the faster the product or cone is heated, the higher the temperature required to mature the product or bend the cone by the same amount. This relationship can be seen in the cone temperature equivalent tables in the Cone Reference Chart. Note that the temperature for the end point of cones increases as the heating rate increases.

 

Determining the Effective Heating Rate

The maturing of most ceramics occurs during the last 100°C of the firing process. This is also true for the bending behavior of a pyrometric cone. Since cones are time-temperature (heat work) indicators, then the heating rate will affect the end point (when the tip reaches a 90° angle) of the cone. Since most firing profiles incorporate a hold time, the actual or effective heating rate must account for this variable. As a rule of thumb, one can calculate the effective heating rate by determining the total time the ware is subjected to the last 100°C in temperature. As an example, assume that the kiln was heated to a top temperature of 1200°C and it took the kiln 2.5 hours to go from 1100°C to 1200°C. If the kiln was held at 1200°C for 1 hour and then cooled from 1200°C to 1100°C in 0.5 hours, then the total time for the top 100°C would be 4 hours. The effective heating rate is estimated by dividing 100°C by 4 or 25°C per hour. Orton provides temperature conversion tables and charts that allow the bending angle to be converted to an equivalent temperature, if the heating rate is known. This allows for determination of temperature differences within a kiln or a kiln car.

 

Hold Time

Hold time also affects the bending or deformation of Pyrometric cones. Generally, firing to an equivalent temperature for a cone and then soaking for about 1-2 hours will be sufficient heat work to deform the next higher cone number. Additional soaking of 4-6 hours will deform the following cone, and some 16-20 additional hours will be required to deform the next higher cone in the series.

 

Kiln Atmosphere

The ceramist knows that kiln atmosphere can have major affect on reactions and the properties of his ware. Since cone deformation is brought about by thermochemical reactions, they can be expected to be affected by the atmosphere in which they are used. Fortunately, the conditions that influence product properties generally have related effects on cone behavior, so that the relative behavior of cones does not change and they are still a useful tool for evaluating temperature distributions within the firing zone of a kiln. The environmental conditions in a kiln most likely to influence cone behavior are:

  • Degree of oxidation or reduction
  • Presence of sulfur gases
  • Presence of water vapor
  • Flame impingement on the cones
  • Radiation effects involving hotter or cooler surfaces nearby
  • Drafts (cool air) in the kiln

 

Reducing atmospheres can have an adverse effect on the deformation behavior of cones. The low temperature cones, containing glass frit with metal compounds, are especially sensitive to reducing conditions. Also, under reducing conditions, the organic binder cannot be fully oxidized and as a result, these cones may bloat and turn black (see Trouble Shooting section for descriptions of cone problems). Bloating will alter cone deformation characteristics. The “red” cones (those containing iron oxide-cones O10 to 3) are also adversely influenced by reducing conditions and will have a green to black appearance after firing.

 

All cones that do not contain lead or iron oxide (cones O19 through O11, “Iron Free” O10 through 3, and cones 4 through 42) can be used satisfactorily in reducing atmospheres provided the organic materials normally present in cones are fully oxidized (burned off) before resorting to a reducing atmosphere. Heating cones to 800-850°F in air will burn off the organic binders. PCE Cones or cones which are pre-calcined have been successfully employed where the entire firing is under neutral or reducing atmospheres.

 

Cones and most ceramics will generally mature sooner, or at a lower temperature, when fired in a reducing atmosphere as compared with oxidizing conditions. Pre-calcining cones may alter deformation characteristics if they are heated into a region where glass begins to form, so users requiring such treatment should establish their own procedures and controls through testing.

 

The practice of “flashing” a kiln (alternate oxidizing and reducing atmospheres) does not normally have an adverse effect on cone deformation.

 

Kiln atmospheres which are either sulphurous or reducing may cause some cones to develop a rigid “shell” with an interior that becomes fluid, therefore, producing erratic deformation. This shell occurs due to a change in the chemical composition of the cone surface.

 

Improved Iron-Free Cones, O4 through 3 (available since 1976) and all cones hotter than cone 3 may be used satisfactorily in a sulphurous atmosphere.

 

“Hard shelling” may also be encountered with regular cones O10 through O3 in a high velocity or prolonged firing in a combustion atmosphere. This type of “hard shelling” is caused by volatilization of boric oxide from one of the raw materials, glass frit, in the presence of high moisture air. “Hard shelling” causes cones to deform at higher than normal temperatures. Severely “hard shelled” cones do not bend in an arc but fall over stiffly like a fallen tree. They have a dry matte surface and sharp edges.

 

The improved Iron-Free Cones, O10 through 3 (available since 1976) are free of boric oxide containing frit and thus do not “hard shell” from this cause.

 

The presence of water vapor, particularly in large quantities, will also influence cone behavior. In fact, even in small amounts, it can cause a cone to deform sooner than normal. The reason for this is that water vapor diffuses into ceramic materials during firing and causes changes in the vitrification process¹. This is the main reason that cones exhibit a different behavior in electric and non-muffled gas kilns. Even though water vapor in the products of combustion can run as high as 19%, it does not necessarily detract from the usefulness of cones because comparable behavior usually occurs in the properties of the ware.

 

Other Firing Conditions

Fly ash from solid fuel may settle on the cone and to some extent influence its deformation. Likewise, volatile products such as salt fumes, lead, and zinc compounds may produce a surface glaze on the cone, which may or may not influence behavior. The cutting action of flames can cause cones to develop melted tips or behave in other cause abnormal ways. If possible, cones should be protected from flame impingement and kiln drafts.

 

Radiation from hotter surfaces, or, if the cones are placed close to cooler surfaces, may also affect cone deformation, and, so far as is practical, cones should be protected from this condition as should the ware.

 

1. Effect of Atmospheres in Firing Ceramics – C.J. Koenig Published by the Columbia Gas System Service Corp., Columbus, Ohio and the Southern California Gas Co., Los Angeles, California

Be the first to submit a review on this product!
Review and Rate this Item
Send this product to a friend...