10 Mesh Flint Grog (coarse)

10 mesh Flint Grog. Considered to be a coarse mesh grog. Grog is incorporated into clay bodies to give texture, impart 'bite' when throwing, to assist drying, or to increase firing strength. It will reduce the rate of clay shrinkage during drying and, in...

30 Mesh Flint Grog (fine)

30 mesh Flint Grog. Considered to be a fine mesh grog. Grog is incorporated into clay bodies to give texture, impart 'bite' when throwing, to assist drying, or to increase firing strength. It will reduce the rate of clay shrinkage during drying and, in...

Kyanite (100 mesh)

Kyanite is a super-duty refractory material with very high resistance to thermal shock. It is widely employed in insulating brick, kiln furniture, refractory shapes, etc. and in body formulations used in porcelain, tile bodies, and...

Kyanite, 35 Mesh

Type a description for this product here...

Molochite (120 mesh)

Molochite is a pure white made-made granular material. The granules are hard and refractory. It is made by firing raw low-iron kaolin to very high temperatures (about 1500℃) to bring about maximum conversion of the clay crystal to crystalline mullite...

Molochite (200 mesh)

Molochite is a pure white made-made granular material. The granules are hard and refractory. It is made by firing raw low-iron kaolin to very high temperatures (about 1500℃) to bring about maximum conversion of the clay crystal to crystalline mullite...

Molochite (30 mesh)

Molochite is a pure white made-made granular material. The granules are hard and refractory. It is made by firing raw low-iron kaolin to very high temperatures (about 1500℃) to bring about maximum conversion of the clay crystal to crystalline mullite...

Mulcoa, 20 mesh

Type a description for this product here...

Mullite, 100 mesh

Mullite, 35 mesh

Mullite, 48 mesh

Type a description for this product here...

Silica Shot

Also called Silica Sand. Used in clay bodies instead of grog. Many sizes and particle shapes are available. It is not appropriate to include the chemistry of silica sand in body calculations because the silica does not participate in the chemistry of...